Optically tuned poly (3-hexylthiophene-2,5-diyl) P3HT/PCBM (modified fullerene) blend for plastic solar cell

Nanotechnology-assisted organic electronics is a wide-spread and promising research field at present in the search for an efficient solar cell. The strong absorption spectra of the donor polymer poly[3-hexylthiophene-2,5-diyl)(P3HT) in the visible region and the prominent absorption of the acceptor [6,6]-phenyl C61 butyric acid methyl ester(PCBM) in UV region have proved them to be the most popular donor-acceptor pair for preparing photoactive materials. The active blend, having a broad absorption spectrum, is the primary requisite for an efficient solar cell. The present work is focused on optimizing the photoactive blend of (P3HT)) and PCBM for the maximum absorption of the solar energy. P3HT: PCBM blends of weight ratio 3:1, 1:1 & 1:3 were prepared in xylene as the solvent and glass coated samples are prepared by solution cast method. Samples were characterized by JASCO UV Vis NIR V 670 spectrometer. P3HT has strong absorption in the visible region, while PCBM has an effective absorption in the UV region with broad tail of absorption extending up to 800 nm. The spectrum for the blend is a superposition of the spectra of the component moieties. The 1:3 blend of P3HT with PCBM has broad spectral sensitivity for absorption and can be used as the best photoactive blend for construction of a plastic solar cell. The energy difference (band gap) between Highest Occupied Molecular Orbital (HOMO) and the Lowest Un-occupied Molecular Orbital (LUMO) of the samples were determined through Tauc’s plot. Calculations from Tauc’s plot indicated that pure P3HT sample has an onset wavelength of 640 nm with a band gap of 1.93 eV. The onset wavelengths for 3:1 & 1:1 blends are almost same of about 632 nm with a band gap of 1.96 eV. The optimized blend 1:3 sample has the onset wavelength 653 nm with the least energy gap 1.9 eV.The absorption by the blend can be further enhanced by either dye sensitization or plasmon resonance.

1. Ritesh Tipnis, Darin Laird, Mathew Mathai. Polymer-based Materials for Printed Electronics: Enabling High Efficiency Solar Power and Lighting. Material Matters, 2008, 3 (4), P. 92.

2. Li G., Vishal Shrotriya, et al. Manipulating regioregular poly (3-hexylthiophene):[6,6]-phenyl-C61-butyric acid methyl ester blends?route towards high efficiency polymer solar cells. Journal of Materials Chemistry, 2007, 17, P. 3126–3140.

3. Mohamad K.A., Afishah Alias, et al. Mixed P3HT/PCBM Organic Thin-Film Transistors: Relation between Morphology and Electrical Characteristics. J. Chem. Chem. Eng., 2014, 8, P. 476–481.

4. Hummelen(Kees) J.C. Improved fullerene materials for plastic photovoltaics. http://www.rug.nl/msc/research/groups/molecularMaterialsDevices.

5. Chirvase D., Parisi J., Hummelen J.C., Dyakonov V. Influence of nanomorphology on the photovoltaic action of polymer-fullerene composites. Nanotechnology, 2004, 15, P. 1317.