Nanosystems: Phys. Chem. Math., 2022, 13 (6), 655–661

Formation of nanocrystalline particles on the basis of La2(Ni,Mn,Fe)2O6 variable composition phases having a structure of double perovskite under conditions of solution combustion

DenisD. Averkiev – Ioffe Institute, St. Petersburg; St. Petersburg State Electrotechnical University “LETI”, St. Petersburg, Russia; swnesli2019@gmail.com
Lyudmila L. Larina – Solar Photovoltaic Laboratory, Emanuel Institute of Biochemical Physics, Moscow, Russia
Oleg I. Shevaleevskiy – Solar Photovoltaic Laboratory, Emanuel Institute of Biochemical Physics, Moscow, Russia; shevale2006@yahoo.com
Oksana V. Almjasheva – Ioffe Institute, St. Petersburg; St. Petersburg State Electrotechnical University “LETI”, St. Petersburg, Russia; almjasheva@mail.ru

Corresponding author: Oksana V. Almjasheva, almjasheva@mail.ru

DOI 10.17586/2220-8054-2022-13-6-655-661

ABSTRACT Nanocrystalline particles on the basis of La2(Ni,Mn,Fe)2O6 variable composition phases of a double perovskite structure have been produced by glycine-nitrate combustion. The size of crystallites grows from 5 to 45 nm with an increase in iron content of synthesized particles. It is demonstrated that iron unevenly builds into octahedral sites of nickel and manganese ions substituting mainly manganese ions. At the same time, the dependence of double perovskite unit cell volume on the iron ions concentration is well described by Retgers’ law.

KEYWORDS double perovskite, nanocrystals, solution combustion, photovoltaics.

ACKNOWLEDGEMENTS The authors express their gratitude to V. V. Gusarov for the attention he paid to the work. X-ray diffraction and SEM was performed using the equipment of the Engineering Center of Saint Petersburg State Institute of Technology. This study was financially supported by the Russian Science Foundation (project no. 20-63-47016).

FOR CITATION Averkiev D.D., Larina L.L., Shevaleevskiy O.I., Almjasheva O.V. Formation of nanocrystalline particles on the basis of La2(Ni,Mn,Fe)2O6 variable composition phases having a structure of double perovskite under conditions of solution combustion. Nanosystems: Phys. Chem. Math., 2022, 13 (6), 655–661.

Download

[In Russian] Д.Д. Аверкиев, Л.Л. Ларина, О.И. Шевалеевский, О.В. Альмяшева

Формирование в условиях растворного горения нанокристаллических частиц на основе фаз переменного состава La2(Ni,Mn,Fe)2O6 со структурой двойного перовскита

УДК 544.22

АННОТАЦИЯ Методом глицин-нитратного горения получены нанокристаллические частицы на основе фаз переменного состава La2(Ni,Mn,Fe)2O6 со структурой двойного перовскита. Размер кристаллитов увеличивается от 5 до 45 нм с увеличением содержания железа в синтезируемых частицах. Показано, что железо неравномерно встраивается в октаэдрические позиции ионов никеля и марганца, замещая преимущественно ионы марганца. При этом зависимость объёма элементарной ячейки двойного перовскита от концентрации ионов железа хорошо описывается правилом Ретгерса.

КЛЮЧЕВЫЕ СЛОВА двойной перовскит, нанокристаллы, растворное горение, фотовольтаика.