NANOSYSTEMS: PHYSICS, CHEMISTRY, MATHEMATICS, 2013, 4 (6), P. 834–843

THE EFFECT OF FULLERENE C60 ON THE MECHANICAL AND DIELECTRICAL BEHAVIOR OF EPOXY RESINS AT LOW LOADING

D.V. Pikhurov – National Research University of Information Technologies, Mechanics and Optics, 49 Kronverkskiy pr., 197101 Saint Petersburg, Russian Federation; firus07@rambler.ru
V.V. Zuev – National Research University of Information Technologies, Mechanics and Optics, 49 Kronverkskiy pr., 197101 Saint Petersburg; Institute of Macromolecular Compounds of the Russian Academy of Sciences, 31 Bolshoi pr., 199004 Saint Petersburg, Russian Federation; zuev@hq.macro.ru

Fullerene C60 / epoxy polymers nanocomposites with different C60 loadings (0.01-0.12 wt. %) have been prepared. Mechanical testing shows that compared with the neat epoxy, the mechanical and toughening properties of the composites are greatly improved. The addition of fullerene C60 increased the modulus of the epoxy (up to 20 %), but the glass transition temperature was unaffected. The measured impact strength was also increased, from 38 to 115 kJ/m2 with the addition of 0.12 wt.% of fullerene C60. The toughening mechanism has been discussed. Dielectric spectroscopy was used to investigate the influence of nanoparticles on the relaxation processes in the polymer matrix.

Keywords: epoxy resins, fullerene C60, nanocomposites, mechanical properties; dielectric spectroscopy; relaxation processes.

PACS 81.07.Lb

Download

2 responses to 11


  1. The following time I read a weblog, I hope that it doesnt disappoint me as much as this one. I mean, I know it was my option to read, but I actually thought youd have one thing interesting to say. All I hear is a bunch of whining about something that you can repair in case you werent too busy on the lookout for attention.

  2. Edgarmah

    pinup azerbaycan: pin-up casino giris – pin-up oyunu

Leave a Reply

Your email address will not be published.

You may use these HTML tags and attributes: <a href="" title=""> <abbr title=""> <acronym title=""> <b> <blockquote cite=""> <cite> <code> <del datetime=""> <em> <i> <q cite=""> <strike> <strong>