Nanosystems: Phys. Chem. Math., 2024, 15 (1), 130–134
Sorption of polar and non-polar liquids by GO powders according to DSC experiments
Alexander V. Kaplin – Moscow State University, Chemistry Department, Moscow; Semenov Federal Research Center of Chemical Physics, Russian Academy of Sciences, Moscow, Russia; alex1997kaplin@mail.ru
Elena A. Eremina – Moscow State University, Chemistry Department, Moscow, Russia; ea_er@mail.ru
Mikhail V. Korobov – Moscow State University, Chemistry Department, Moscow, Russia; mkorobov49@gmail.com
Corresponding author: Alexander V. Kaplin, alex1997kaplin@mail.ru
PACS 68.43.-h
DOI 10.17586/2220-8054-2024-15-1-130-134
ABSTRACT The sorption properties of Hummers (HGO) and Brodie (BGO) graphite oxides with respect to various liquids were studied by the DSC method. In the case of HGO, the reduced material (RHGO) was obtained by hydrothermal synthesis. The effective reduction of the material was confirmed by XRD. The difference in the sorption of water and acetonitrile by HGO and RHGO was experimentally observed. The DSC experimental procedure was developed to estimate the selective sorption of the component from the immisible liquid mixtures. The procedure has been tested on the sorption of the water-octane mixture by HGO. It was shown that water can be sorbed by HGO from the mixture in an amount equal to equilibrium sorption of pure water by HGO at 273 K. The results obtained will serve as the basis for further studies of the sorption properties of GO.
KEYWORDS graphite oxide, sorption, DSC
ACKNOWLEDGEMENTS The study was supported by the Russian Science Foundation (RSF 22-29-00544).
FOR CITATION Kaplin A.V., Eremina E.A., Korobov M.V. Sorption of polar and non-polar liquids by GO powders according to DSC experiments. Nanosystems: Phys. Chem. Math., 2024, 15 (1), 130-134.
[In Russian] А.В. Каплин, Е.А. Еремина, М.В. Коробов
Сорбция полярных и неполярных жидкостей порошками GO по данным ДСК
УДК 549.212
АННОТАЦИЯ В данной работе методом ДСК исследованы сорбционные свойства оксидов графита (метод Хаммерса (HGO) и метод Броди (BGO)) по отношению к различным жидкостям. В случае HGO восстановленный материал (RHGO) был получен методом гидротермального синтеза. Эффективное восстановление материала было подтверждено методом РФА. Показаны различия в сорбции воды и ацетонитрила в HGO и RHGO. Также в данной работе разработана методика оценки селективной сорбции воды из водно-октановой смеси материалом HGO методом ДСК. Показано, что вода может сорбироваться HGO в количестве, соответствующем равновесной сорбции при температуре плавления воды из водно-октановой смеси. Полученные результаты послужат основой для дальнейших исследований сорбционных свойств GO.
КЛЮЧЕВЫЕ СЛОВА оксид графита, сорбция, ДСК