Nanosystems: Phys. Chem. Math., 2024, 15 (3), 410–417
The effect of layered silicates on the morphological, rheological and mechanical properties of PA and PP blends
Qodirbek Nuridin ugli Berdinazarov – Institute of Polymer Chemistry and Physics, Uzbekistan Academy of Sciences, Tashkent, Uzbekistan; qodirberdinazarov@mail.ru
Elshod Olmosovich Khakberdiev – Institute of Polymer Chemistry and Physics, Uzbekistan Academy of Sciences, Tashkent, Uzbekistan; profhaqberdiyev@gmail.com
Nigmat Rustamovich Ashurov – Institute of Polymer Chemistry and Physics, Uzbekistan Academy of Sciences, Tashkent, Uzbekistan; nigmat.ashurov@gmail.com
Corresponding author: Q. Berdinazarov, qodirberdinazarov@mail.ru
PACS 83.80.Tc, 82.35.Np, 82.35.Lr
DOI 10.17586/2220-8054-2024-15-3-410-417
ABSTRACT We study rheological, morphological and mechanical properties of polyamide-6 (PA) and polypropylene (PP) blends in the presence of layered silicates (two types of organically modified montmorillonite – Cloisite30B for PA and Cloisite20A for PP). For comparison, we used maleic anhydride grafted polypropylene (PP-g-MA) as a compatibilizer and in all compositions weight ratio of PA and PP was constant 80/20, respectively. Introduction of layered silicates always led to more viscous melt and increased storage modulus. It is also identified that layered silicates cause more finer-dispersed morphology than PP-g-MA. Elastic modulus and yield strength were increased when the layered silicates were introduced in either composites or blends.
KEYWORDS Polyamide-6, polypropylene, montmorillonite, polymer composite, polymer blend, compatibilizer
ACKNOWLEDGEMENTS The authors acknowledge prof. Paula Moldenaers and her SMaRT team for their assistance in conducting practical experiments. The study was financed by the project of ”Nanocomposite polymerpolymer blend materials on the basis of polyolefins produced in Uzbekistan”.
FOR CITATION Berdinazarov Q., Khakberdiev E., Ashurov N. The effect of layered silicates on the morphological, rheological and mechanical properties of PA and PP blends. Nanosystems: Phys. Chem. Math., 2024, 15 (3), 410–417.
[In Russian] Кодибек Н. Бердиназаров, Элшод О. Хакбердиев, Нигмат Р. Ашуров
Влияние слоистых силикатов на морфологические, реологические и механические свойства смеси ПА и ПП
АННОТАЦИЯ Изучены реологические, морфологические и механические свойства смесей полиамида-6 (ПА) и полипропилена (ПП) в присутствии слоистых силикатов (двух типов органически модифицированного монтмориллонита – Cloisite30B для ПА и Cloisite20A для ПП). Для сравнения мы использовали полипропилен с привитым малеиновым ангидридом (ПП-г-МА) в качестве компатибилизатора, и во всех композициях массовое соотношение ПА и ПП было постоянным 80/20 соответственно. Введение слоистых силикатов всегда приводило к более вязкому расплаву и увеличению модуля упругости. Также установлено, что слоистые силикаты имеют более тонкодисперсную морфологию, чем ПП-г-МА. Модуль упругости и предел текучести увеличивались при введении слоистых силикатов либо в композиты, либо в смеси.
КЛЮЧЕВЫЕ СЛОВА Полиамид-6, полипропилен, монтмориллонит, полимер композит, полимерная смесь, компатибилизатор